LTH 1922

LTH 1922

Low Density Polyethylene

Product Description

LTH 1922 has been manufactured using SABTEC licensed technology

Additives

  • Antioxidant

Applications

  • LTH 1922 is specially developed for applications that require a good balance between flow
    properties and mechanical properties, e.g. toys, household articles, clamping lids.

Features

Test Method Unit Typical Value Typical Properties
Polymer Properties
ISO 1133 dg/min 22 MFI (190 °C /2 .16 Kg )
ISO 1133 dg/min 75 MFI (190 °C/5 Kg )
ISO 1133 ml/10min 29 MVR (190 °C /2 .16 Kg )
ISO 1133 ml/10min 98 MVR (190 °C /5 Kg )
ISO 1183 (A) Kg/m3 919 Density
Thermal Properties
ISO 527-1, -3 % 250/600 Heat deflection temperature at 0.45MPa (HDT/B)
ASTM D 1709 g 110 Vicat softening temperature at 10N (VST/A)
ISO 306 94 Melting Point
ASTM D 1003 % <8.0 Enthalpy change
Mechanical properties
ISO 527/2 MPa 8 Stress at yield
ISO 527/2 MPa 7 Stress at break
ISO 527/2 % 400 Strain at break
ISO 527/2 MPa 175 Tensile modulus
ISO 899 MPa 80 Creep modulus (After 1 hour)
ISO 899 MPa 45 Creep modulus (After 1000 hour)
ISO 180 A KJ/m2 42 Notched lzod at +23°C
ISO 180 A KJ/m2 5 Notched lzod at -30 °C
ISO 8256/1B KJ/m2 86 Notched Tensile impact strength
ISO 8256/1B % 8.4 Elongation at break
ISO 8256/1B MPa 16 Maximum Tension
ISO 868 - 3 Hardness Shore D
Ball indentation test
ISO 2039-1 N 49 Applied load
ISO 2039-1 MPa 16 Ball indentation hardness
SABTEC Method h 3 ESCR